Transport
Rust-anode primer
Unique technology for industrial galvanization, rich in organic zinc through electrochemical bonding with 88% zinc content in the dry layer. Offers a lifespan comparable to hot-dip galvanization under the same exposure conditions.
Available sizes: 2 and 12 kilograms.
- Mono-component product
- 99.995% pure organic zinc
- Lower in VOCs 285 grams/litre
- Cathodic protection due to electrochemical bond with the metal
- Easy to apply with standard painting equipment, including electrostatic
- Can be applied on non-friable rust, free of dust
- Can be covered with most paint products
- Can be used in duplex over new and old HDG or metallization
- Rust-Anode® Primer comes in only one colour: flat grey natural zinc RAL # 7005
- An equal dry film thickness of Rust-Anode® Primer provides the same performance as hot dip galvanization or metallization.
- No structural distortion
- Flexibility
- Permanent adhesion
- No cathodic disbondment
- Follow thermal expansions
- Moisture cured, without dew point
- High resistance to saltwater and salty environments
- Can be applied to aluminum, stainless, corten, cast iron, (all metals), concrete and existing paint after minimal cleaning
- Resists to hydrocarbons such as hydraulic fluid, diesel, gasoline, urea, etc.
- Dries quickly (hygro-reactive) in moist environments
- Can be used at any time to retouch Rust-Anode® Primer coated surfaces
- Can be applied at temperatures from –5°C and +37°C (23°F to +98°F)
- Meets ASTM B117 (Salt Spray Test), ASTM D522 (Mandrel Bend Test), CAN/CGSB 1-GP-71 Method 119.5 and CAN/CGSB 1.181 and Canadian Food Inspection Agency standards
| Consult document here |
- An outstanding elasticity and plasticity of the dry film that allow the expansion and bending of the metal substrate;
- A total and permanent metalizing bonding to the metal substrate;
- A good resistance to impact;
- A resistance to abrasion of high performance;
- A superior resistance to hydrocarbons and salt damages;
- Single pack formulation, easy to mix;
- lt allows the same corrosion protection as hot-dipped galvanizing and metalizing with equal dry film thickness’s
- Little change of colour in the time;
- Application from -5 C (+23°F) to + 37 C (+98°F);
- Resist to mist and to rain, 90 min. after application;
- Application without taking account of dew point;
- Minimal surface preparation;
- Resistance where pH is between 5.5 and 12.5;
- The Rust-Anode Primer can be used without a top coat;
- Easy application with any standard painting equipment spray gun or electrostatic.
Chlor-Rid
- Remove chlorides, sulfates, nitrates and other soluble salt contaminants
- Leaves no film or residue after use
- Biodegradable, Water Soluble, Non-Toxic
Available in certain Sherwin-Williams stores.
HoldTight® 102
- Prevents Flash Rusting, Wet or Dry Blasted Surfaces
- Removes All Surface Salts
- Biodegradable, Water Soluble, Non-Toxic
Website: https://holdtight.com/products/holdtight-102/
(American clients)
Hold*Blast
- Surface passivator
- Prevent Flash Rusting, Wet or Dry Blasted Surfaces
- Biodegradable
- Environmentally safe
Available in certain Sherwin-Williams stores.
MET-L PHOS 272
Anti-oxidant to remove rust or light scale on steel surfaces.
View the sheet here.
MC2000
Particularly effective degreaser on aluminium.
View the sheet here.
SRS Environnement
Quebec : 418 831-8808
Fax : 418 831-5055
Canada / USA : 1-888-SRS-SOLV
Email: info@srsenv.com
377 Rue Dupuy
Québec (QC)
G1L 1P2
Metering pump |
 |
| More information |
Salt Test |
 |
| More information |
Wet gage and electronic Gauge
| Wet gage :used to measure the wet thickness of the applied product |
| Electronic gauge: Used to measure the dry thickness of the coating. | |
 |  |
Comparative table
| Hot-Dip Galvanization | Rust-Anode® Primer | |
|---|---|---|
|
Active cathodic protection |
|
|
|
Zinc dry film thickness control |
|
|
|
Protection longevity |
|
|
|
Surface uniformity |
MAY VARY |
|
|
Minimal process time |
MAY VARY |
|
|
Minimal substrate preparation |
|
|
|
Weldability |
|
|
|
Touch up at any time |
|
|
|
Easy to apply |
|
|
|
Application with standard paint equipment |
|
|
|
Low energy-consuming process |
|
|
|
Salt-resistance |
|
|
|
Salted water immersion |
|
|
|
Applicable on various metals: |
||
|
On new steel |
|
|
|
On rusty steel (brown) |
|
|
|
On a new hot-dip galvanization or metallization |
|
|
|
On old hot-dip galvanizing or metallization |
|
|
|
On aluminum |
|
|
|
On Copper |
|
|
|
On cast iron |
|
|
|
On cast aluminum |
|
|
|
On concrete |
|
|
|
On corten steel |
|
|
|
Health Canada approval |
|
|
|
Bending flexibility of galvanized parts |
|
|
|
Equivalent protection performance as hot dipped galvanized |
|
|
|
Process with No delay to your production schedule |
|
|
Questions and answers
Yes, please refer to the technical data sheet or contact our experts to learn more about the application method.
Drying and curing/application time for a wet film thickness of 5.0 mils (125µm) at 77°F (25°C) with 50% relative humidity (RH). The product is touch dry in 45 minutes. The curing time may vary depending on ambient temperature and relative humidity. A minimum of 30% relative humidity is required during application for proper drying and curing. For more information, refer to the technical data sheet.
Mix thoroughly at low speed until complete homogenization, do not use automatic paint shakers. With our mixing kit, the mixing time ranges from 2 to 3 minutes.
Rust-Anode Primer can be applied with standard painting equipment.